Description
|
SPECIFICATON OF DIPPED CONVENTIONAL POLYESTER TYRE CORD FABRIC |
||||||||||
|
NO. |
ITEMS |
UNITE |
1000D/2 |
1300D/2 |
1000D/3 |
1500D/2 |
2000D/2 |
1300D/3 |
1500D/3 |
|
|
(1100dtex/2) |
(1440dtex/2) |
(1100dtex/3) |
(1670dtex/2) |
(2200dtex/2) |
(1440dtex/3) |
(1670dtex/3) |
||||
|
1 |
Ave Breaking Stength (min) |
N/end |
140 |
180 |
205 |
205 |
280 |
260 |
305 |
|
|
2 |
Elongation @ certain load |
% |
4.5+1.0 (44.1 N) |
4.5+1.0 (58.0 N) |
4.5+1.0 (66.6 N) |
4.5+1.0 (66.6 N) |
4.5+1.0 (88.2 N) |
4.5+1.0 (88.2 N) |
4.5+1.0 (100 N) |
|
|
3 |
Adhension(H-test)(min) |
N/Cm |
125 |
135 |
140 |
140 |
170 |
165 |
180 |
|
|
4 |
Breaking strength difference(max) |
% |
4 |
4 |
4 |
4 |
4 |
4 |
4 |
|
|
5 |
Breaking elongation difference(max) |
% |
5 |
5 |
5 |
5 |
5 |
5 |
5 |
|
|
6 |
Dip pick up |
% |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
|
|
7 |
Breaking elongation |
% |
15+/-2 |
15+/-2 |
15+/-2 |
15+/-2 |
15+/-2 |
15+/-2 |
15+/-2 |
|
|
8 |
Diameter |
mm |
0.56+0.03 |
0.61+0.03 |
0.66+0.03 |
0.66+0.03 |
0.75+0.03 |
0.74+0.03 |
0.81+0.03 |
|
|
9 |
Twist |
Single(Z) |
T/10cm |
45+1.5 |
40+1.5 |
37+1.5 |
37+1.5 |
33+1.5 |
33+1.5 |
31+1.5 |
|
Ply twist(S) |
45+1.5 |
40+1.5 |
37+1.5 |
37+1.5 |
33+1.5 |
33+1.5 |
31+1.5 |
|||
|
10 |
Hot air shrinkage 177℃×2min x 0.05CN/dtex (max) |
% |
3 |
3 |
3 |
3 |
3 |
3 |
3 |
|
|
11 |
Elongation @ Breaking of weft yarn (Min) |
% |
120 |
120 |
120 |
120 |
120 |
120 |
120 |
|
SPECIFICATION OF DIPPED HMLS POLYESTER TYRE CORD FABRICS
|
NO. |
ITEMS |
UNITE |
1000D/2 |
1300D/2 |
1000D/3 |
1500D/2 |
2000D/2 |
1300D/3 |
1500D/3 |
|
|
(1100dtex/2) |
(1440dtex/2) |
(1100dtex/3) |
(1670dtex/2) |
(2200dtex/2) |
(1440dtex/3) |
(1670dtex/3) |
||||
|
1 |
Ave Breaking Stength (min) |
N/end |
140 |
180 |
205 |
205 |
280 |
260 |
305 |
|
|
2 |
Elongation @ certain load |
% |
4.5+1.0 (44.1 N) |
4.5+1.0 (58.0 N) |
4.5+1.0 (66.6 N) |
4.5+1.0 (66.6 N) |
4.5+1.0 (88.2 N) |
4.5+1.0 (88.2 N) |
4.5+1.0 (100 N) |
|
|
3 |
Adhension(H-test)(min) |
N/Cm |
125 |
135 |
140 |
140 |
170 |
165 |
180 |
|
|
4 |
Breaking strength difference(max) |
% |
4 |
4 |
4 |
4 |
4 |
4 |
4 |
|
|
5 |
Breaking elongation difference(max) |
% |
5 |
5 |
5 |
5 |
5 |
5 |
5 |
|
|
6 |
Dip pick up |
% |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
3.0+1 |
|
|
7 |
Breaking elongation (Min.) |
% |
14 |
14 |
14 |
14 |
14 |
14 |
14 |
|
|
8 |
Diameter |
mm |
0.56+0.03 |
0.61+0.03 |
0.66+0.03 |
0.66+0.03 |
0.75+0.03 |
0.74+0.03 |
0.81+0.03 |
|
|
9 |
Twist |
Single(Z) |
T/10cm |
45+1.5 |
40+1.5 |
37+1.5 |
37+1.5 |
33+1.5 |
33+1.5 |
30+1.5 |
|
Ply twist(S) |
45+1.5 |
40+1.5 |
37+1.5 |
37+1.5 |
33+1.5 |
33+1.5 |
30+1.5 |
|||
|
10 |
Hot air shrinkage 177℃×2min x 0.05CN/dtex (max) |
% |
2 |
2 |
2 |
2 |
2 |
2 |
2 |
|
|
11 |
Elongation @ Breaking of weft yarn (Min) |
% |
120 |
120 |
120 |
120 |
120 |
120 |
120 |
|